200/201
Wst. 2.4066 / 2.4068
UNS N02200 / N02201
Nickel 99.2 / LC-nickel 99.2
Stock program: Available on request
Specification: ASTM B 161/B 163
EN 10216-5
Maximum expose temperature: 360°C /680°F
Nickel 200 and nickel 201 are solid solution strengthened, commercially pure 99% nickel alloy. Nickel 201 was a modification of 200 to control carbon (0.02% max), this lower carbon content reduces hardness and makes the alloy 201 suitable for cold-formed items and use at higher temperatures. The elemental restrictions of both resulting in a single alloy with the desired characteristics of both alloys, nickel 200/201. Nickel 200 and nickel 201 are combined into one dual-certified chemistry.
Characteristics:
- High resistance to various reducing chemicals
- Widely used to handle caustic soda
- Resistance to numerous organic solutions and caustic lye
- Good resistance to neutral and alkaline salt solutions
- Resistance to hydrochloric acid and chlorination of hydro carbons as benzene, methane and ethane
Market applications:
- Petrochemical industry
- Salt production plants
- Floor and chloric processing
- Food production
- Marine and offshore engineering
Technical details
| Technical composition (%) | Fe | Ni | Mn | Cu | Si | C | S | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 200 | min | – | 99.0 | – | – | – | – | – | |||||||
| max | 0.40 | – | 0.35 | 0.25 | 0.35 | 0.150 | 0.010 | ||||||||
| 201 | min | – | 99.0 | – | – | – | – | – | |||||||
| max | 0.40 | – | 0.35 | 0.25 | 0.35 | 0.020 | 0.010 | ||||||||
| Mechanical properties | 200 | 201 | ||
|---|---|---|---|---|
| Tensile strenght (mpa, min) nl | 380 | 345 | ||
| Yield strength (0.2% offset mpa, min) | 100 | 80 | ||
| Elongation (%, min) | 40 | 40 | ||
| Density / weight (g / cm3 / kg) | 8.89 | 8.89 |