316Ti

Wst. 1.4571

UNS S31635

Stock program: 3 – 42 mm OD

Specification:
EN 10216-5/EN10305/TSI 15156-3/EN ISO 1127 D4/T3 – D3/T3
NACE MR0175/PED 97/23 EC

Maximum service temperature: 500°C / 930°F

316Ti is a titanium stabilized version of 316L molybdenum bearing austenitic stainless steel. This results in a better high temperature strength and mechanical strength, but equivalent corrosion resistance to sensitization. It’s not typical free machining grade and there for not recommended. For difficult high speed machining processing.  Sensitization resistance is achieved with the addition of titanium to stabilize the structure of 316Ti  against chromium carbide precipitation, which is the source of the sensitization.

Characteristics:

  • Good corrosion and pilling resistance
  • Good resistance at higher temperature
  • Good impact strength on cryogenic temperatures down to minimal -200°C  /-325°F
  • High creep, stress-rupture and tensile strength at elevated temperature

Market applications:

  • Chemical & petrochemical equipment
  • Pharmaceutical
  • Food & Beverage
  • Brewery
  • Shipbuilding
  • Heat exchangers

Technical details

Technical composition (%) Fe Cr Ni Mo Mn Si P N C S Ti
316Ti min Bal. 16.0 10.0 2.0
max 18.0 14.0 3.0 2.00 0.75 0.450 0.10 0.080 0.030 5x% C+N
Mechanical properties 316Ti
Tensile strenght (mpa, min) nl 500 -730
Yield strength (0.2% offset mpa, min) 210
Elongation (%, min) 35
Density / weight (g / cm3 / kg) 8.0